Large-Scale Epitaxial Integration of Single-Crystalline BiSb Topological Insulator on GaAs (111)A - LAAS-Micro Nano Bio Technologies Access content directly
Journal Articles ACS Applied Electronic Materials Year : 2024

Large-Scale Epitaxial Integration of Single-Crystalline BiSb Topological Insulator on GaAs (111)A

Abstract

Topological insulators (TI) are promising materials for future spintronics applications and their epitaxial integration would allow the realization of new hybrid interfaces. As the first materials studied, Bismuth Antimony alloys (Bi1-xSbx) show great potential due to their tuneable electronic band structure and efficient charge-to-spin conversion. Here, we report the growth of Bi1-xSbx thin films on GaAs (111)A substrates following two different protocols. For the conventional epitaxy process, the grown films show excellent crystallinity and twin domains corresponding to an in-plane 180° rotation of the crystalline structure. Domain walls are found to be composition-dependent and have a lower density for Antimony-rich films. For the optimized process, depositing an Antimony bilayer prior to BiSb growth allows achieving single crystallinity of the TI films. The topologically protected surface states are evidenced by ex-situ ARPES measurements for domains-free and conventional films. To the best of our knowledge, this work presents the first large-scale epitaxial integration of single crystalline Bi1-xSbx thin films on industrial substrates.
Fichier principal
Vignette du fichier
Full_Manuscript.pdf (1.15 Mo) Télécharger le fichier
Origin Files produced by the author(s)

Dates and versions

hal-04584442 , version 1 (23-05-2024)

Licence

Identifiers

Cite

Mohamed Ali Khaled, Leonardo Cancellara, Salima Fekraoui, Richard Daubriac, François Bertran, et al.. Large-Scale Epitaxial Integration of Single-Crystalline BiSb Topological Insulator on GaAs (111)A. ACS Applied Electronic Materials, 2024, ⟨10.1021/acsaelm.4c00400⟩. ⟨hal-04584442⟩
44 View
7 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More